UNS N08020鎳基合金
產(chǎn)品名稱：ALLOY20/UNS N08020
國際通稱：Alloy 20合金、UNS N08020、NS143、Inconel alloy20/NAS 335X、W.Nr.2.4460
Nicrofer 3620 Nb-alloy20、ATI 20
各國標(biāo)準(zhǔn)：ASTM B463/ ASME SB463、ASTM A240/ ASME SA240、ASTM B729/ ASME SB729
主要成分：
| Element | Wt, % |
|---|---|
| Carbon [C] | ≤0.07 |
| Manganese [Mn] | ≤2.00 |
| Phosphorus [P] | ≤0.045 |
| Sulfur [S] | ≤0.035 |
| Silicon [Si] | ≤1.00 |
| Nickel [Ni] | 32.00~38.00 |
| Chromium [Cr] | 19.00~21.00 |
| Molybdenum [Mo] | 2.00~3.00 |
| Copper [Cu] | 3.00~4.00 |
| Niobium+Tantalum [Nb+Ta] | 8xCarbon~1 |
| Iron | Remainder |
*The tabulated values are abstracted from ASTM B462 Gr. UNS N08020.
物理性能：
| Alloy | Tensile Strength, min. | Yield Strength, min. | Elongation, min. | Reduction of Area, min. | ||
|---|---|---|---|---|---|---|
| ASTM B462 | ksi | MPa | ksi | MPa | % | % |
| UNS N08020 | 80 | 551 | 35 | 241 | 30.0 | 50.0 |
*All values shall be measured at room temperature.
*Alloy 20 flanges shall be supplied in stabilized-annealed condition.
熱處理：900-1150℃之間保溫1-2小時，快速空冷或水冷。
機械性能：抗拉強度：σb≥550Mpa，屈服強度σb≥240Mpa：延伸率：δ≥30%，硬度；HB135-220
耐腐蝕性及主要使用環(huán)境：
Alloy 20合金具有很多優(yōu)異性能的耐蝕合金，對氧化性和中等還原性腐蝕 有很好的抵抗能力，具有優(yōu)異的抗應(yīng)力腐蝕開裂能力和好的耐局部腐蝕能力在很多化工工藝介質(zhì)中有滿意的耐蝕特性。
有優(yōu)異的抗應(yīng)腐蝕開裂能力和好的耐局部還原性復(fù)合介質(zhì)腐蝕，運用于硫酸環(huán)境及含有鹵族離子及金屬離子的硫酸溶液工業(yè)裝置。
配套焊接材料及焊接工藝：Alloy 20合金的焊接建議采用AWS A5.14焊絲ERNiCrMo-3或AWS A5.11焊條ENiCrMo-3，焊接工藝及指導(dǎo)書歡迎來電索取。
應(yīng)用領(lǐng)域有：硫酸酸洗設(shè)備、磷酸生產(chǎn)設(shè)備、石油化工裝備、煤化工、海洋平臺、海水淡化、復(fù)合板、波紋管膨脹節(jié)等行業(yè)和產(chǎn)品。